Ferrite Magnets are composed of iron oxide, barium and strontium elements. Compared with other Non-Rare-Earth Magnets, Ferrite Magnets have higher flux density, greater coercive force, and better corrosion resistance. As one of our most popular products, Ferrite Magnets have an additional advantage because of their low cost. To make sure that Ferrite Magnets can be used despite of their hard and brittle nature, LIHE always applies special machining techniques while manufacturing.
Specifications for Ferrite Magnets (Sintered)
Materials | Br(mT) | Hcb(Ka/m) | HcJ(Ka/m) | (BH)max(Kj/m3) |
SJ285 | SJ/T10410 |
| Y8T | 200-235 | 125-160 | 210-280 | 6.5-9.5 |
| Y20 | 320-380 | 135-190 | 140-195 | 18.0-22.0 |
| Y22H | 310-360 | 220-250 | 280-320 | 20.0-24.0 |
| Y23 | 320-370 | 170-190 | 190-230 | 20.0-25.4 |
| Y25 | 360-400 | 135-170 | 140-200 | 22.5-28.0 |
| Y26H | 360-390 | 220-250 | 225-255 | 23.0-28.0 |
| Y27H | 370-400 | 205-250 | 210-255 | 25.0-29.5 |
| Y28 | 370-400 | 175-210 | 180-220 | 26.0-30.0 |
| Y30H-1 | 380-400 | 230-275 | 235-290 | 27.0-32.0 |
| Y30H-2 | 395-415 | 275-300 | 310-335 | 28.5-32.5 |
| Y32 | 400-420 | 160-190 | 165-195 | 30.0-33.5 |
| Y33 | 410-430 | 220-250 | 225-255 | 31.5-35.0 |
Specifications for Ferrite Magnets (Bonded)
TYPE | Br(MT) | HCb(KA/M) | HCJ(KA/M) | BH(max)KJ/M3 | Forming Methods | LHJC-1 | 130-180 | 80-115 | 100-160 | 3.2-6.4 | Extrusion | LHJC-2 | 210-235 | 140-160 | 200-220 | 9.5-10.4 | Extrusion | LHYY-1 | 130-180 | 80-120 | 100-160 | 4.0-6.4 | Calendar | LHYY-2 | 180-220 | 100-140 | 120-190 | 6.4-8.0 | Calendar | LHYY-3 | 210-239 | 140-165 | 150-210 | 8.0-10.4 | Calendar | LHYY-4 | 240-265 | 156-181 | 200-270 | 10.4-12.5 | Calendar
|
|